Alloy A286 (AMS 5731/ AMS 5732 / AMS 5737 / AMS 5525)
Alloy A286 bar can be solution treated at the temperatures detailed below, rapid cooled and then age hardened at 1325ºF (720ºC) for 16 hours and air cooling. The 1800ºF (980ºC) solution treatment produces the highest creep-rupture strength in age-hardened material whereas the 1650ºF (900ºC) treatment results in improved ductility and room ...
ASM Material Data Sheet - MatWeb
Allegheny Ludlum Altemp A286 alloy is an iron-base superalloy useful for applications requiring high strength and corrosion resistance up to 704 degrees Celsius and for lower stress applications at high temperatures. Specific uses include jet engine nacelles, parts, and fasteners.
Stainless Steel A286 - Tech Steel & Materials
Stainless Steel A286 is a precipitation-hardenable super-alloy based on iron. The material finds use in applications requiring high strength, paired with corrosion resistance up to 1300 °F (700 °C).
Super Alloy A-286 (UNS S66286) - AZoM.com
Super alloy A-286 is hardened by the cold working process and is also capable of being age hardened due to the presence of titanium in this alloy. Super alloy A-286 is solution annealed at 982°C (1800°F), oil quenched, held for 16 h at 718°C (1325°F) and finally cooled in air. This heat treatment improves the strength of super alloy A-286.
286 stainless steel is a precipita on-hardenable super-alloy based on iron. A-286 stainless steel finds use in applica ons requiring high strength, paired with corrosion resistance up to 1300 °F (700 °C).
A286 Tech Data - High Temp Metals
Alloy A-286 is designed for applications requiring high strength and good corrosion resistance at temperatures up to 1300 °F (704 °C). This alloy offers high ductility in notched sections. In fact, the notched rupture strength of alloy A-286 is superior to many other commercial alloys with comparable high temperature properties.
A286 Aircraft Steel - Aircraft Materials
Alloy A286 bar can be solution treated at the temperatures detailed below, rapid cooled and then age hardened at 1325ºF (720ºC) for 16 hours and air cooling.
A286 AMS 5731 AMS 5732 AMS 5737 - AEON
HARDNESS. In the solution treated condition, hardness is 140 - 180 Brinell. After aging the hardness increases to 248 - 321 Brinell. The hardness is affected by the titanium content and the aging temperature. FORGEABILITY/ FORMABILITY. A-286 alloy has forgeability similar to many austenitic stainless steels.
ATI A286 ™ Alloy - atimaterials.com
ATI A286 ™ Alloy is typically supplied in the solution annealed condition. The mechanical properties in this condition are 105 ksi (724 MPa) max. tensile strength, 25% min. elongation, and a maximum hardness of 90 HRB.
Stainless Steel A286 AMS 5737 | Tech Steel & Materials
AMS 5737 is a sub-type specification of Stainless Steel A286, a precipitation-hardenable super-alloy with high strength at elevated temperatures, good corrosion resistance up to 1300 °F (700 °C), and excellent non-magnetic strength at cryogenic temperatures, down to -320 °F (-196 °C).